URN:NBN:SI:DOC-060FF1GK2024Du, XiaomingLi, TianfuMa, MingMa, XueSun, ZhendongWang, Zhijundocuments/doc/0/URN_NBN_SI_doc-060FF1GK_001.pdfdocuments/doc/0/URN_NBN_SI_doc-060FF1GK_001.txt358articlestr. 285–29310.17222/mit.2023.10441580-2949198696707URN:NBN:SI:doc-060FF1GKengInštitut za kovinske materiale in tehnologijeMateriali in tehnologijeInCCu-rich precipitatefracture mechanismizločki bogati na bakrumehanizem porušitvemodel alloymodelna zlitinaspinodal decompositionspinodalni razpadtermično staranjethermal agingEffect of long-term thermal aging at 475 °C on embrittlement of Fe-32Cr-4Ni-4Cu model alloyVpliv dolgotrajnega termičnega staranja pri 475 °C na krhkost modelne zlitine Fe-32Cr-4Ni-4Cu