17 KB184 KB15 KB200020242010Lamut, JakobOruč, MirsadaPihura, Dervišletnik:44številka:5str. 235-238ISSN:1580-2949COBISSID:828586URN:URN:NBN:SI:doc-7DFMZK6FenInštitut za kovinske materiale in tehnologijeMateriali in tehnologijegrodeljjeklomanganoksidacijažlindraSelective oxidation of manganese in molten pig iron| Selektivna oksidacija mangana v staljenem grodlju|An examination of the process of selective oxidation for molten pig iron indicates the possibility of lowering the content of unwanted or harmful elements. This process makes it possible to achieve the optimum Mn content in pig iron (hot metal) without any oxidation of the other elements present, suchas carbon, etc. Several variants of oxygen blowing with the addition of a slag-forming component were checked. The final element content in the hot metal depends on the initial Mn content, the oxygen blowing and on the added slag components. The lowering of the Mn content in the hot metal to the limit solves the problems of converter processing, lowers the slag quantity, increases the yield of steel by more 4 % and improves the steel-making processAnaliza procesa selektivne oksidacije tekočega grodlja daje možnost, da odstranimo neželene in škodljive elemente. Proces omogoča, da dosežemo optimalno vsebnost mangana v surovem grodlju (vroča kovina) brez oksidacije drugih elementov, ogljika in drugih. Preizkušenih je bilo več variant vpihovanja kisika z dodatki za tvorbo žlindre. Končna vsebnost mangana v grodlju je odvisna od začetne vsebnosti, vpihovanja kisika in od dodatkov za žlindranje. Zmanjšanje vsebnosti mangana do meje rešuje probleme konvertorskega procesiranja, zmanjša količino žlindre, poveča izkoristek jekla za več od 4 % in izboljša proces izdelave jeklaTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije