14 KB333 KB11 KB200020242013Sert, YeşimToplan, Nilštevilka:2letnik:47str. 181-183ISSN:1580-2949COBISSID:978602URN:URN:NBN:SI:doc-E4XVDOMOenInštitut za kovinske materiale in tehnologijeMateriali in tehnologijealuminijev oksiddebele plastikromov oksidobrabaplazemski nanos z brizganjemtitanov dioksidtribologijaTribological behaviour of a plasma-sprayed Al203-TiO2-Cr2O3 coating| Tribološko ponašanje s plazmo napršenega Al2O3-TiO2-Cr2O3 nanosa|Alumina-titania, titania, chromia and chromia-titania coatings, deposited on aluminium substrates with atmospheric, plasma-spray, coating techniques (APSCTs), were tested on a low-frequency reciprocating-sliding tribometer. The surface wear of the coatings was investigated with SEM and optical microscopy. The denser Crsub{2}Osub{3} coatings showed a higher wear resistance than themore porous Alsub{2}Osub{3}-TiOsub2 and TiOsub2 coatings. An increase in the titania content diminishes the coating hardness and the wear resistanceNanosi Alspodaj{2}Ospodaj{3}-TiOspodaj2, TiOspodaj2, Crspodaj{2}Ospodaj3, Crspodaj{2}Ospodaj3-TiOspodaj2 atmosferskim plazemskim z nanašanjem z brizganjem (APSCT) na podlago iz aluminija so bili preizkušeni na nizkofrekvenčnem protismernem drsnem tribometru. Obrabljena površina nanosa je bila preiskovana s SEM in svetlobno mikroskopijo. Gostejši nanos Crspodaj{2}Ospodaj{3} je pokazal večjo odpornost proti obrabi kot bolj porozna nanosa Alspodaj{2}Ospodaj3-TiOspodaj2 in TiOspodaj2. Povečanje vsebnosti TiOspodaj2 zmanjšuje trdoto nanosa in zmanjša odpornost proti obrabiTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije