24 KB611 KB23 KB200020242000Golobič, IztokPerovnik, Vladimirštevilka:1/2letnik:346 stranistr. 47-52ISSN:1580-2949COBISSID:213674URN:URN:NBN:SI:doc-FX65VTKWslInštitut za kovinske materiale in tehnologijeMateriali in tehnologijejeklokaljenjemikrostrukturaohlajevalne krivuljetrdotaNapovedovanje trdote jekel po kaljenju| Forecasting hardness of steels after quenching|In this paper the influence of chemical composition on austenite transformation in TTT diagrams of steels 20MnCr5 and 27MnSiVS6 is described. Computer programed predicting of cooling rate and properties after quenching is successful if two microstructures are formed. On border areas, where formed microstructures and their quantities are strongly dependent on cooling rate, predicting is less accurateV članku opisujemo raziskave vpliva legirnih elementov na transformacijo avstenita v TTT-diagramih za jekla 20MnCr5 in 27MnSiVS6. Napovedovanje ohlajevalnih hitrosti in lastnosti po kaljenju z računalniškim programom in TTT-diagramom je uspešno v primeru, kadar nastajata dve mikrostrukturi. Na mejnih področjih, kjer se pri majhnih spremembah ohlajanja močno spreminja število nastalih mikrostruktur in njihova količina, je napovedovanje manj natančnoTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije