22 KB855 KB17 KB199920252010Klobčar, DamjanKosel, FrancMuhič, MitjaTušek, Janezletnik:56številka:6str. 351-356ISSN:0039-2480COBISSID:11559963URN:URN:NBN:SI:doc-ZIEHEDKBenAssociation of Mechanical Engineers and Technicians of Slovenia et al.Zveza strojnih inženirjev in tehnikov Slovenije et al.Strojniški vestnikaluminijeve zlitinealuminium alloymikrostrukturaorodjatlačno litjetrdotaAnalysis of die casting tool material|This paper deals with defects produced in aluminium alloy die casting dies during die operation. The most frequent defect is thermal fatigue cracking. Hardness and toughness is measured on specimens cut from different parts of used die casting die. The results show a significant difference in material microstructure and hardness between the surface and the core. The intense martensite tempering is observed on the die surface, while the core material microstructure remains unchanged. A considerable hardness drop is measured on the material surface and no change is observed in the depth of six millimetres from surfaceČlanek obravnava napake, ki nastajajo na orodju pri tlačnem litju aluminijevih zlitin med obratovanjem. Najpogostejše napake so razpoke zaradi toplotnega utrujanja. Trdota in žilavost sta bili izmerjeni na vzorcih izrezanih iz različnih delov rabljenega orodja. Rezultati kažejo znatno razlikov mikrostrukturi in trdoti materiala med površino in notranjostjo orodja. Na površini orodja smo opazili močno popuščen martenzit, medtem ko je mikrostruktura materiala v notranjosti ostala nespremenjena. Na površini materiala je bil izmerjen občuten padec trdote na globini nad šest milimetrov pa se trdota ni spremenilaTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaUniverza v Ljubljani, Fakulteta za strojništvo