ISSN 1318-0010 KZLTET 32(3-497)165(1998) EXPERIMENTAL STUDY OF STEEL BEHAVIOUR IN PROCESS OF MUSHY STATE DEFORMATION EKSPERIMENTALNI [TUDIJ PROCESA DEFORMACIJE JEKLA V KA[ASTEM STANJU JAROSLAV HORSKY1, M. RAUDENSKY1, P. KOTRBAČEK1, B. ŠARLER2 1Technical University of Brno, Czech Republic 2LFDT, University of Ljubljana, Slovenia Prejem rokopisa - received: 1998-11-25; sprejem za objavo - accepted for publication: 1998-12-07 The aim of the experiments was to measure the steel resistance to the tool indentation in mushy state (i.e. between the solidus and liquidus) in dependence on the tool position and to evaluate the influence of the temperature and that of the rate of loading on the history of forces acting on the tool. Key words: steel, mushy state, resistance, forces on the tool Namen predstavljenih poskusov je meriti odpor vdiranja orodja v ka{asto stanje jekla (med solidus in likvidus temperaturo) v odvisnosti od položaja orodja in oceniti vpliv temperature in hitrosti obtežbe na časovni potek sil, ki delujejo na orodje. Ključne besede: jeklo, kašasto stanje, odpor, sile na orodje 1 INTRODUCTION In order to determine a constitutive model suitable for the simulation of the mushy state metal deformation, experimental testing providing material characteristics is required. In the temperature range of the semi-liquid area, the environment changes progress from a fully solid zone (solid curve) to a completely liquid zone (liquid curve). The changes in the composition of these two phases are followed by the changes in material rheology which results in the necessity to apply dynamically appropriate physical laws so that the material could be described in each instant. The behaviour of metals and other materials can be described using different mathematical-physical relations, however a thixotropic substance cannot be described by a single equation1,2. 2 THEORY OF EXPERIMENT x - position v - velocity T - temperature The series of measurements it repeated for the same temperatures, but different velocities of motion. 3 EXPERIMENTAL MATERIAL Tool carbon steel was tested. It has a low content of additions (Table 1), which enables to study its parameters using the equilibrium metastable binary diagram Fe-C. Table 1: Chemical composition of steel Tabela 1: Kemična sestava jekel ELEMENT C (%) Mn (%) Si (%) CONTENT 0.95-1.10 0.20-0.35 0.30 The sum of equations used for the modelling of mushy state steel forming includes about 20 parameters that need to be determined or specified. Therefore, an experimental program was prepared verifying the influence of the following factors: - influence of the penetration speed, - influence of the percentage contents of solid and liquid phase on the penetration force. The experiment was conducted for a series of constant temperatures between the temperature of solidus (TS) and that of liquidus (TL). The dependence of force on position at a constant temperature and velocity is the result of each measurement: F = fce (x); v,T = constant F - force It is obvious from the diagram that the solidus temperature for the given steel is approximately 1346°C and L if + 5 y + S ~ 1340 °C austenit Y J460°C Liq ----Ûiàft® x^i îq ■ + y ----~~ ^----"Liq. + FejC 1 solidus solidus ledeburit + austenit ledeburit +F"e,C' Sv+F^C" a ferit perlit + + I perlit 19191 + Fe3C " perlit + FeyC " + + ledeb u rit transf. ledeburit trans/. + Fe}C' H • /-<■,<••"-' _^_^_{%]C 6.6B Diagram 1: Equilibrium metastable binary diagram Fe-C Diagram 1: Ravnotežni metastabilni dvosestavinski diagram Fe-C KOVINE, ZLITINE, TEHNOLOGIJE 32 (1998) 3-4 165 J. HORSKY ET AL.: EXPERIMENTAL STUDY OF STEEL BEHAVIOUR.. Figure 1: Principal scheme of the experimental apparatus: 1-load frame INSTRON, 2-load frame cross beam, 3-dynamometer, 4-tool chucking head, 5-furnace, 6-resistance heating elements, 7-thermocouple, 8-tool, 9-specimen - melted-down metal, 10-refractory concrete base Slika 1: Osnovna shema eksperimenta: 1-obtežilni okvir INSTRON, 2-prečni drog obtežilnega okvirja, 3-silomer, 4-prižemna glava orodja, 5-peč, 6-uporovni grelni elementi, 7-termočlen, 8-orodje, 9-vzorec -raztaljena kovina, 10-podstavek Figure 2: Resistance furnace scheme: 1-ceramic insulation CERACHEM, 2-resistance heating element SUPERKANTHAL, 3-tool (Al2O3), 4-thermocouple (Pt-PtRh13), 5-steel sample, 6-crucible (Al2O3), 7-refractory concrete base Slika 2: Shema uporovne peci: 1-keramična izolacija CERACHEM, 2-uporovni grelni element SUPERKANTAL, 3-orodje (Al2O3), 4-termočlen (Pt-PtRh13), 5-jeklen vzorec, 6-talilnik (a12O3), 7-podstavek the liquidus temperature 1465°C (see Diagram 1 Fe3C). The difference between the temperatures is about 120°C. The theoretical contents of the solid and liquid phase were computed using the "lever rule". 4 INDENTATION TEST Description of the experimental apparatus for the indentation test The basic part of the stand is formed by load frame INSTRON, (Figure 1) newly equipped with a position measuring device and a HOTTINGER dynamometer with a range up to 2000 N. The inner structure of the furnace placed in the frame is shown in Figure 2. The furnace has a special design allowing to reach the mushy state of steels and to access the sample-area both from the top and the bottom side. The heated elements are made from SUPERKANTHAL. The control thermocouple is placed close to the sample of the material. The measurement is carried out for two tool types of different diameters, 5 and 10 mm. The inside diameter of the crucible is Do = 27 mm. By the ratio Do/D > 5 the forming becomes similar to the indentation into the halfspace. The maximum length of the tool indented into the melted metal during the experiment is about 5o mm, (Figure 3). 498 By the tool diameter of 10 mm the ratio of the crucible diameter to that of the tool is Do < 5 in this case the forging becomes similar to the back extrusion3. Indentation test procedure (see Figure 5) - a sample is placed into the furnace and it is heated to a temperature corresponding to the melting-down b) Figure 3: The initial and final position of the needle during the experiment: a) initial position, b) final position; 1-tool, 2-semi-liquid metal, 3-crucible Slika 3: Začetni in končni položaj igle pri eksperimentu: a) začetni položaj, b) končni položaj; 1-orodje, 2-kovina v kašastem stanju, 3-talilnik KOVINE, ZLITINE, TEHNOLOGIJE 32 (1998) 6 J. HORSKY ET AL.: EXPERIMENTAL STUDY OF STEEL BEHAVIOUR.. Figure 4: Experiment diagram: 1-load frame cross beam, 2-dynamometer HOTTINGER, 3-tool chucking heat, 4-argon inlet, 5-tool (Al2O3), 6-projective tube, 7-ceramic seal, 8-secondary programmable controller MICROTHERM, 9-secondary thermocouple (Pt-PhRh13), 10-primary programmable controller MICROTHERM, 11-primary thermocouple (Pt-PtRh13), 12-ceramic crucible (Al2O3), 13-specimen Slika 4: Diagram eksperimenta: 1-precni drog obtežilnega okvirja, 2-silomer HOTTINGER, 3-prižemna glava orodja, 4-vstop argona, 5-orodje (Al2O3), 6-usmerilna cev, 7-keramicno tesnilo, 8-sekundarni programirni nadzor, 9-sekundarni termoclen (Pt-PtRh13), 10-primarni programirni nadzor, 11-primarni termoclen (Pt-PtRh13), 12-keramicni talilnik (Al2O3), 13-vzorec loading 5 and 50 cm/min. for a tool with a diameter of fD = 10 mm (see the appendixes A, B). The diagram of the force-position dependence obtained by the indentation test can be divided into two sections. In the first section, the force is constant until the instant of the tool touching the melted metal. For the second section, an exponential growth of the force is characteristic (see appendixes A, B). In the experiments with other temperature or loading rate, the second part of the curve is shifted to higher or lower force values. Still, the character of the loading history is preserved. 5 HOT UPSETTING TEST The experimental apparatus was additionally equipped to enable the hot upsetting test of a steel cylinder at very high temperatures corresponding to the melting of the specimen (see Figure 8). The first approach -the indentation of a thin tool into steel in semi-solid state, can be used at higher temperatures, i.e. also for a larger liquid phase in the specimen. The stress in the thin tool increases quickly with the increasing content of the solid phase, and may cause its failure. On the conrtary, the temperature, at which the liquid content reaches a value where the tested cylinder cannot keep its original shape and gets destroyed due to the gravity, limits the second test. These two methods enable to study the steel - the temperature in the furnace is decreased to a value prescribed for the experiment - the needle is indented into the sample with a selected speed of motion and data describing the instant position of the needle and the instant force acting on the needle are monitored (the upper part of the furnace with low voltage wiring and the projecting part of the tool) - the sample is heated to a temperature where the liquid state is reached - now, the motion is reversed and the needle is moved into the starting position. (Position of the needle during the experiment can be seen in Figure 3). Example of obtained results A steel with a solidus temperature of 1340°C and a liquidus temperature of 1460°C was selected as experimental material. Two examples of experimental force recordings were selected in: the material temperatures range from 1450°C down to 1410°C. The percentage of the solid fraction varies from 10% to 65% and it is described in detail in the appendixes. Resistance values were measured for velocities of loading 5 and 50 cm/min. for a tool with a diameter of fD = 5 mm and then for two velocities of j ,2 Jt A 5 _____6 -—J_ Figure 5: Resistance furnace scheme for the hot upsetting test: 1-ceramic insulation CERACHEM, 2-resistance heating elements, 3-refractory concrete tool, 4-thermocouple (Pt-PtRh13), 5-refractory concrete cover, 6-ground ceramic discs (Al2O3), 7-refractory concrete base, 8-tested cylinder, 9-inert atmosphere inlet Slika 5: Shema uporovne peci pri: 1-keramicna izolacija, 2-uporovni grelni element, 3-orodje, 4-termoclen (Pt-PtRh13), 5-pokrov podstavka, 6-keramicna diska (Al2O3), 7-podstavek, 8-valjni preizkušanec, 9-vstop interne atmosfere 499 KOVINE, ZLITINE, TEHNOLOGIJE 32 (1998) 6 J. HORSKY ET AL.: EXPERIMENTAL STUDY OF STEEL BEHAVIOUR.. i 2 3 - v- i -\--- ~ ~ A Figure 6: Hot upsetting test in detail: 1-refractory concrete tool, 2-ground ceramic discs (Al2O3), 3-tested cylinder, 4-inert atmosphere inlet Slika 6: Podrobnost testiranja vro~ega posedanja: 1-podstavek, 2-podložna kerami~na diska, 3-valjni preizkušanec, 4-vstop inertne atmosfere behaviour within the whole temperature range between the liquidus and solidus curves. Description of the experimental apparatus for the hot upsetting test The furnace was adapted for the hot upsetting test. The detail of experimental specimen used for the hot upsetting test is presented in Figure 6. The steel sample is cylindrical and the ratio sample diameter over height is do/v = 1,6. The sample diameter is then 15 mm and its height is 24 mm. The tested steel sample is placed on a corundum fine-grained ceramic disc with a ground surface. The massive support under the specimen is made of refractory concrete. Protective atmosphere is led through the refractory concrete directly to the steel sample. The tool diameter is 29 mm and it is made of refractory concrete. The steel sample is loaded through a second corundum disc by the tool (see Figure 6). Three hot upsetting tests were conducted for a temperature of 1369°C (10% of the liquid phase), 1388°C (20% of the liquid phase), 1405°C (30% of the liquid phase) and 1418°C (40% of the liquid phase). Hot upsetting test procedure - The tested cylinder is placed in the furnace and it is heated up to the required temperature in inert atmosphere. - The tool is set into the starting position (10 mm above the specimen) (Figure 7a). - The temperature in the furnace is homogenised (homogenisation time is 30 min.). - The velocity of the tool is set (hot upsetting rate v = 0.5 cm/min.). - The tested cylinder is upset using the pre-set rate and data on the instantaneous position of the tool and the instantaneous force acting on the tool are recorded (see Figure 7b). The mentioned system of force and position scanning enables a simultaneous transmission of data into the computer. - The specimen is deformed to a 1/3 of its original length and after stopping the motion of the tool, the relaxation of the tested cylinder is measured (Figure 7c). - The motion is reversed and the tool is moved back to the initial position. - The measurement is repeated for a different upsetting temperature. The dependence force-position (see Figure 8) is characteristic of the initial increase in force. In the following section, the material relaxation and the force reduction can be observed. In the final section, the force grows exponentially up to the maxim value. The force grows with the increasing diameter of the upset cylinder. After releasing the motion, the force decreases instantly and the material in mushy state relaxes. ACKNOWLEDGEMENTS The experiments presented here were supported by the project COPERNICUS, contract number OK 380290/2110/3422: "Computer aided process simulation of iron mushy state forming", with contribution of the Figure 7: Hot upsetting test: 1-refractory concrete tool, 2-ceramic discs, 3-tested cylinder, 4-inert atmosphere inlet a) initial position of the tool - (T=const. ;v=0) b) hot upsetting of the tested cylinder - (T=const.;v=0,5cm/min.) c) final position of the tool - (T=const.; v=0) Slika 7: Testiranje vro~ega posedanja: a) za~etni položaj orodja, b) posedanje, c) kon~ni položaj orodja; 1-podstavek, 2-kerami~ni ploš~ici, 3-valjni preizkušanec, 4-vstop inertne atmosfere 500 KOVINE, ZLITINE, TEHNOLOGIJE 32 (1998) 6 J. HORSKY ET AL.: EXPERIMENTAL STUDY OF STEEL BEHAVIOUR.. Czech-Slovene cooperation project ME 380266/ Appendix B 2110/3422. Appendix A Influence of temperature (of the solid friction) on the history of forces acting on the tool with a diameter of 5 mm. The experiments are carried out for three rates of loading 5 and 50 cm/min, (for detailed description see the diagrams and their captions below). Diagrams showing the influence of temperature (of the solid fraction) on the history of forcing acting on the tool with a diameter of 10 mm. Measured for two rates of loading 5 a 50 cm/min, (for detailed description see the diagrams and their captions below). Velocity=5cm/min. S5 ® 100 / t=1 « t=1 « t=1 u t=1 450°C, 440°C. 430°C, 420°C. f„= 1 0 fs=36 f.=48 f,=58 k 5 S F /, / / // — t=1 41 0°C, fs=65 S // 7 / /j / / / A // 30 40 Position [mm] Diagram (Appendix A): Distribution of forces required for the indentation of tool of a diameter of 5 mm and rate of loading 5 cm/min. Diagram (Priloga A): Porazdelitev sil potrebnih za vtis orodja premera 5 mm s hitrostjo obtežbe 5 cm/min Velocity = 5cm/min. Fat S 100 \ <-» t=i « t=i « t=i 450°C. 440°C, 430°C, fs= 1C fs=36 fs=48 % / / / 1 / /V 30 40 Position [mm] Diagram (Appendix B): Distribution of forces required for the indentation of tool of a diameter of 50 mm and rate of loading 5 cm/min. Diagram (Priloga B): Porazdelitev sil potrebnih za vtis orodja premera 50 mm s hitrostjo obtežbe 5 cm/min Diagram (Appendix A): Distribution of forces required for the indentation of tool of a diameter of 5 mm and rate of loading 50 cm/min. Diagram (Priloga A): Porazdelitev sil potrebnih za vtis orodja premera 5 mm s hitrostjo obtežbe 50 cm/min Diagram (Appendix B): Distribution of forces required for the indentation of tool of a diameter of 50 mm and rate of loading 50 cm/min. Diagram (Priloga B): Porazdelitev sil potrebnih za vtis orodja premera 50 mm s hitrostjo obtežbe 50 cm/min 501 KOVINE, ZLITINE, TEHNOLOGIJE 32 (1998) 6 J. HORSKY ET AL.: EXPERIMENTAL STUDY OF STEEL BEHAVIOUR.. Appendix C The results of the measurements are presented in the following Figures 8 and 9. Figure 8: Dependence of the load force on the deformation of the tested cylinder during the hot upsetting test for a ontent of the liquid phase 10%, 20%, 30% and 40% Slika 8: Vpliv utežne sile na deformacijo valjnega preizkušanca pri poskusu vročega posedanja za vsebnost kapljevinske faze 10%, 20%, 30% in 40% 6 REFERENCES 'V. Laxmanan, M. C. Flemings: Deformation of semi-solid Sn-15%Pb alloy, Metallurgical Transaction A, 11A (1980) dec Figure 9: Time history of the load force during the hot upsetting test for a content of the liquid phase of 10%, 20%, 30% and 40% Slika 9:Casovni potek utežne sile za vsebnost kapljevinske faze 10%, 20%, 30% in 40% 2 M. Kiuchi, S. Sugizama: A New Process to Manufacture Semi-Solid Metals, Proceedings of the Second Int. Conf., Eds Brown and Flemings, 1992, 47-56 3 M. Forejt: Teorie tvareni, Vysoke učeni technicke v Brne, Nakladatel-stvi Vysokeho uceni technickeho v Brne, 1992 502 KOVINE, ZLITINE, TEHNOLOGIJE 32 (1998) 6