Interpenetrating polymer networks were synthesised from anionic polyurethane and cationic acrylic prepolymers with different amounts of incorporated ionic groups. Their morphology was determined by differential scanning calorimetry.

Rights

URN

URN:NBN:SI:DOC-X3RA6K1Z

COBISS ID

1362458

Added

22.07.2011

Metadata

Citation

APA:

Anžlovar, Alojz, Anžur, Irena, Malavašič, Tatjana (1995). Morfologija prepletenih polimernih mrež v odvisnosti od vgrajenih ionskih skupin, volume 29, issue 1/2. URN:NBN:SI:DOC-X3RA6K1Z from http://www.dlib.si

MLA:

Anžlovar, Alojz, Anžur, Irena, Malavašič, Tatjana. Morfologija prepletenih polimernih mrež v odvisnosti od vgrajenih ionskih skupin. Inštitut za kovinske materiale in tehnologije
Železarna Jesenice
Železarna Ravne
Železarna Štore, 1995.
<http://www.dlib.si/?URN=URN:NBN:SI:DOC-X3RA6K1Z>

Kovine zlitine tehnologije
1992-1999
(Assembly record)

prejšnja

Priprava membran iz delno kristaliničnega poliamida 6,6
1995
(Previous issue)

naslednja

Preizkusi anaerobnega lepila za izdelavo vakuumskih komponent
1995
(Next issue)